Here is the photo of the recovered pellets from the High Power tests.... Only the pellets showing noticable expansion or distortion are shown.... the others looked like they could literally be reused....

Top row is .22 cal, from left to right:
Predator Polymag - 7 pieces
Hunter Extreme - crosscut nose in 3 parts, plus skirt
Baracuda Hunter - nose nearly peeled off
Crow Magnum - nose completely folded over, center punched out



Middle row is .25 cal, from left to right:
Predator Polymag - 8 pieces
Hunter Extreme - mushroomed with 4 jagged edges from crosscut
Mr. HollowPoint 58.8 gr. - nearly completely mushroomed
Crow Magnum - nose section inverted and separated, but was sitting over the skirt

Bottom row, also .25 cal, left to right:
EunJin Dome - some shortening, slight expansion
Mr. HollowPoint 50.0 gr. - completely mushroomed
H&N Ram Point - some shortening, lip at base of point forced back

Note: the H&N Ram Point had a small horizontal lip at the base of the point which acted a bit like a wadcutter and that is what caused the larger entry hole and wider cone shape of the wound channel.... The thin rim around the plastic tip on the Polymags blew apart into many small pieces at these velocities (950-1000 fps).... IMO they are at their best at a lower speed.... and in fact that may apply to all of the hollowpoint pellets, they are starting to come apart.... The Mr. Hollowpoint bullets, on the other hand look very interesting, they are behaving like a PB bullet (not surprising).... It will be interesting to see how they perform at higher velocities and energies....

Bob